Set-Delayed Cement Compositions Comprising Pumice and Associated Methods

ABSTRACT

A variety of methods and compositions are disclosed, including, in one embodiment, a method of cementing in a subterranean formation, comprising: providing a set-delayed cement composition comprising water, pumice, hydrated lime, and a set retarder; activating the set-delayed cement composition; introducing the set-delayed cement composition into a subterranean formation; and allowing the set-delayed cement composition to set in the subterranean formation.

BACKGROUND

Cement compositions may be used in a variety of subterranean operations.For example, in subterranean well construction, a pipe string (e.g.,casing, liners, expandable tubulars, etc.) may be run into a well boreand cemented in place. The process of cementing the pipe string in placeis commonly referred to as “primary cementing.” In a typical primarycementing method, a cement composition may be pumped into an annulusbetween the walls of the well bore and the exterior surface of the pipestring disposed therein. The cement composition may set in the annularspace, thereby forming an annular sheath of hardened, substantiallyimpermeable cement (i.e., a cement sheath) that may support and positionthe pipe string in the well bore and may bond the exterior surface ofthe pipe string to the subterranean formation. Among other things, thecement sheath surrounding the pipe string functions to prevent themigration of fluids in the annulus, as well as protecting the pipestring from corrosion. Cement compositions also may be used in remedialcementing methods, for example, to seal cracks or holes in pipe stringsor cement sheaths, to seal highly permeable formation zones orfractures, to place a cement plug, and the like.

A broad variety of cement compositions have been used in subterraneancementing operations. In some instances, set-delayed cement compositionshave been used. Set-delayed cement compositions are characterized byremaining in a pumpable fluid state for an extended period of time(e.g., at least about 1 day to about 2 weeks or more). When desired foruse, the set-delayed cement compositions should be capable of beingactivated whereby reasonable compressive strengths are developed. Forexample, a cement set accelerator may be added to a set-delayed cementcomposition whereby the composition sets into a hardened mass. Amongother things, the set-delayed cement composition may be suitable for usein well bore applications, for example, where it is desired to preparethe cement composition in advance. This may allow, for example, thecement composition to be stored prior to its use. In addition, this mayallow, for example, the cement composition to be prepared at aconvenient location and then transported to the job site. Accordingly,capital expenditures may be reduced due to a reduction in the need foron-site bulk storage and mixing equipment. This may be particularlyuseful for offshore cementing operations where space onboard the vesselsmay be limited.

While set-delayed cement compositions have been developed heretofore,challenges exist with their successful use in subterranean cementingoperations. For example, set-delayed cement compositions prepared withPortland cement may have undesired gelation issues which can limit theiruse and effectiveness in cementing operations. Other set-delayedcompositions that have been developed, for example, those comprisinghydrated lime and quartz, may be effective in some operations but mayhave limited use at lower temperatures as they may not developsufficient compressive strength when used in subterranean formationshaving lower bottom hole static temperatures.

SUMMARY

An embodiment of the present invention provides a method of cementing ina subterranean formation. The method may comprise providing aset-delayed cement composition comprising water, pumice, hydrated lime,and a set retarder. The method may further comprise activating theset-delayed cement composition. The method may further compriseintroducing the set-delayed cement composition into a subterraneanformation. The method may further comprise allowing the set-delayedcement composition to set in the subterranean formation.

Another embodiment of the present invention provides a method ofcementing in a subterranean formation. The method may comprise providinga set-delayed cement composition comprising water, pumice, hydratedlime, and a set retarder. The method may further comprise storing theset-delayed cement composition for a period of at least about 1 day. Themethod may further comprise adding a cement set accelerator to theset-delayed cement composition. The method may further compriseintroducing the set-delayed cement composition into a subterraneanformation. The method may further comprise allowing the set-delayedcement composition to set in the subterranean formation.

Another embodiment of the present invention provides a set-delayedcement composition that may comprise water, pumice, hydrated lime, and aset retarder. The set-delayed cement composition may remain in apumbable fluid state for a time period of at least about 1 day.

The features and advantages of the present invention will be readilyapparent to those skilled in the art. While numerous changes may be madeby those skilled in the art, such changes are within the spirit of theinvention.

DESCRIPTION OF PREFERRED EMBODIMENTS

The present invention relates to subterranean cementing operations and,more particularly, in certain embodiments, to set-delayed cementcompositions and methods of using set-delayed cement compositions insubterranean formations.

Embodiments of the set-delayed cement compositions of the presentinvention may generally comprise water, pumice, hydrated lime, and a setretarder. Optionally, the set-delayed cement compositions may furthercomprise a dispersant. Advantageously, embodiments of the set-delayedcement compositions may be capable of remaining in a pumpable fluidstate for an extended period of time. For example, the set-delayedcement compositions may remain in a pumpable fluid state for at leastabout 1 day or longer. Advantageously, the set-delayed cementcompositions may develop reasonable-compressive strengths afteractivation at relatively low temperatures. While the set-delayed cementcompositions may be suitable for a number of subterranean cementingoperations, they may be particularly suitable for use in subterraneanformations having relatively low bottom hole static temperatures, e.g.,temperatures less than about 200° F. or ranging from about 100° F. toabout 200° F.

The water used in embodiments of the set-delayed cement compositions ofthe present invention may be from any source provided that it does notcontain an excess of compounds that may undesirably effect, othercomponents in the set-delayed cement compositions. For example, aset-delayed cement composition may comprise fresh water or salt water.Salt water generally may include one or more dissolved salts therein andmay be saturated or unsaturated as desired for a particular application.Seawater or brines may be suitable for use in embodiments of the presentinvention. Further, the water may be present in an amount sufficient toform a pumpable slurry. In certain embodiments, the water may be presentin the set-delayed cement composition in an amount in the range of fromabout 33% to about 200% by weight of the pumice. in certain embodiments,the water may be present in the set-delayed cement compositions in anamount in the range of from about 35% to about 70% by weight of thepumice. One of ordinary skill in the art with the benefit of thisdisclosure will recognize the appropriate amount of water for a chosenapplication.

Embodiments of the set-delayed cement compositions may comprise pumice.Generally, pumice is a volcanic rock that can exhibit cementitiousproperties, in that it may set and harden in the presence of hydratedlime and water. The pumice may also be ground, for example. Generally,the pumice may have any particle size distribution as desired for aparticular application. In certain embodiments, the pumice may have amean particle size in a range of from about 1 micron to about 200microns. The mean particle size corresponds to d50 values as measured byparticle size analyzers such as those manufactured by MalvernInstruments, Worcestershire, United Kingdom. In specific embodiments,the pumice may have a mean particle size in a range of from about 1micron to about 200 micron, from about 5 microns to about 100 microns,or from about 10 micron to about 50 microns. In one particularembodiment, the pumice may have a mean particle size of less than about15 microns. An example of a suitable pumice is available from HessPumice Products, Inc., Malad, Id., as DS-325 lightweight aggregate,having a particle size of less than about 15 microns. It should beappreciated that particle sizes too small may have mixability problemswhile particle sizes too large may not be effectively suspended in thecompositions. One of ordinary skill in the art, with the benefit of thisdisclosure, should be able to select a particle size for the pumicesuitable for use for a chosen application.

Embodiments of the set-delayed cement compositions may comprise hydratedlime. As used herein, the term “hydrated lime” will be understood tomean calcium hydroxide. The hydrated lime may be included in embodimentsof the set-delayed cement compositions, for example, to form a hydrauliccomposition with the pumice. For example, the hydrated lime may beincluded in a pumice-to-hydrated-lime weight ratio of about 10:1 toabout 1:1 or 3:1 to about 5:1. Where present, the hydrated lime may beincluded in the set-delayed cement compositions in an amount in therange of from about 10% to about 100% by weight of the pumice, forexample. In some embodiments, the hydrated lime may be present in anamount ranging between any of and/or including any of about 10%, about20%, about 40%, about 60%, about 80%, or about 100% by weight of thepumice. In some embodiments, the cementitious components present in theset-delayed cement composition may consist essentially of the pumice andthe hydrated lime. For example, the cementitious components mayprimarily comprise the pumice and the hydrated lime without anyadditional components (e.g., Portland cement, fly ash, slag cement) thathydraulically set in the presence of water. One of ordinary skill in theart, with the benefit of this disclosure, will recognize the appropriateamount of the hydrated lime to include for a chosen application.

Embodiments of the set-delayed cement compositions may comprise a setretarder. A broad variety of set retarders may be suitable for use inthe set-delayed cement compositions useful in the present invention. Forexample, the set retarder may comprise phosphonic acid, phosphonic acidderivatives, lignosulfonates, salts, organic acids, carboxymethylatedhydroxyethylated celluloses, synthetic co- or ter-polymers comprisingsulfonate and carboxylic acid groups, borate compounds, derivativesthereof, or mixtures thereof. In certain embodiments, the set retardersused in the set-delayed cement compositions useful in the presentinvention are phosphonic acid derivatives, such as those described inU.S. Pat. No. 4,676,832, the disclosure of which is incorporated hereinby reference. Examples of suitable set retarders include, among others,phosphonic acid derivatives available from Halliburton Energy Services,Inc., of Duncan, Okla., as Micro Matrix® cement retarder. Generally, theset retarder may be present in the set-delayed cement composition usedin the present invention in an amount sufficient to delay the settingfor a desired time. In some embodiments, the set retarder may be presentin the set-delayed cement compositions in an amount in the range of fromabout 0.01% to about 10% by weight of the pumice. In specificembodiments, the set retarder may be present in an amount rangingbetween any of and/or including any of about 0.01%, about 0.1%, about1%, about 2%, about 4%, about 6%, about 8%, or about 10% by weight ofthe pumice. One of ordinary skill in the art, with the benefit of thisdisclosure, will recognize the appropriate amount of the set retarder toinclude for a chosen application.

As previously mentioned, embodiments of the set-delayed cementcompositions may optionally comprise a dispersant. Examples of suitabledispersants include, without limitation, sulfonated-formaldehyde-baseddispersants and polycarboxylated ether dispersants. One example of asuitable sulfonated-formaldehyde-based dispersant that may be suitableis a sulfonated acetone formaldehyde condensate, available fromHalliburton Energy Services, Inc., as CFR™-3 dispersant. One example ofa suitable polycarboxylated ether dispersant that may be suitable isLiquiment® 514L dispersant, available from BASF Corporation, Houston,Tex., that comprises 36% by weight of the polycarboxylated ether inwater. While a variety of dispersants may be used in accordance withembodiments of the present invention, polycarboxylated ether dispersantsmay be particularly suitable for use in some embodiments. Without beinglimited by theory, it is believed that polycarboxylated etherdispersants may synergistically interact with other components of theset-delayed cement composition. For example, it is believed that thepolycarboxylated ether dispersants may react with certain set retarders(e.g., phosphonic acid derivatives) resulting in formation of a gel thatsuspends the pumice and hydrated lime in the composition for an extendedperiod of time.

In some embodiments, the dispersant may be included in the set-delayedcement compositions in an amount in the range of from about 0.01% toabout 5% by weight of the pumice. In specific embodiments, thedispersant may be present in an amount ranging between any of and/orincluding any of about 0.01%, about 0.1%, 0.5%, about 1%, about 2%,about 3%, about 4%, or about 5% by weight of the pumice. One of ordinaryskill in the art, with the benefit of this disclosure, will recognizethe appropriate amount of the dispersant to include for a chosenapplication.

Other additives suitable for use in subterranean cementing operationsalso may be included in embodiments of the set-delayed cementcompositions. Examples of such additives include, but are not limitedto, weighting agents, lightweight additives, gas-generating additives,mechanical-property-enhancing additives, lost-circulation materials,filtration-control additives, fluid-loss-control additives, defoamingagents, foaming agents, thixotropic additives, and combinations thereofIn embodiments, one or more of these additives may be added to theset-delayed cement composition after storing but prior to placement ofthe set-delayed cement composition into a subterranean formation. Aperson having ordinary skill in the art, with the benefit of thisdisclosure, will readily be able to determine the type and amount ofadditive useful for a particular application and desired result.

Those of ordinary skill in the art will appreciate that embodiments ofthe set-delayed cement compositions of the present invention generallyshould have a density suitable for a particular application. By way ofexample, the set-delayed cement compositions may have a density in therange of from about 4 pounds per gallon (“lb/gal”) to about 20 lb/gal.In certain embodiments, the set-delayed cement compositions may have adensity in the range of from about 8 lb/gal to about 17 lb/gal.Embodiments of the set-delayed cement compositions may be foamed orunfoamed or may comprise other means to reduce their densities, such ashollow microspheres, low-density elastic beads, or otherdensity-reducing additives known in the art. In embodiments, the densitymay be reduced after storing the composition, but prior to placement ina subterranean formation. Those of ordinary skill in the art, with thebenefit of this disclosure, will recognize the appropriate density for aparticular application.

As previously mentioned, the set-delayed cement compositions may have adelayed set in that they remain in a pumpable fluid state for anextended period of time. For example, the set-delayed cementcompositions may remain in a pumpable fluid state for a period of timefrom about 1 day to about 7 days or more. In some embodiments, theset-delayed cement compositions may remain in a pumpable fluid state forat least about 1 day, about 7 days, about 10 days, about 20 days, about30 days, about 40 days, about 50 days, about 60 days, or longer. A fluidis considered to be in a pumpable fluid state where the fluid has aconsistency of less than 70 Bearden units of consistency (“Bc”), asmeasured on a high-temperature high-pressure consistometer at roomtemperature (e.g., about 80° F.) in accordance with the procedure fordetermining cement thickening times set forth in API RP Practice 10B-2,Recommended Practice for Testing Well Cements, First Edition, July 2005.As set forth in Example 4 below, an example composition was preparedthat comprised pumice, 20% hydrated lime, 1.4% dispersant (Liquimen®514L), 1.26% set retarder (Micro Matrix® cement retarder), and 62% water(all % by weight of pumice). After 45 days of storage at ambientconditions, the example composition was mixed with 6% calcium chlorideby weight of the pumice. At 140° F., the example composition had athickening time (time to 70 Bc) of 2 hours and 36 minutes and developed50 psi compressive strength in 9 hours and 6 minutes as measured on anUltrasonic Cement Analyzer (“UCA”), available from Fann InstrumentCompany, Houston, Tex., while maintained at 3000 psi. After 48 hours,the sample was crushed and had a compressive strength of 2,240 psi.

When desired for use, embodiments of the set-delayed cement compositionsmay be activated (e.g., by combination with a cement set accelerator) tothereby set into a hardened mass. By way of example, embodiments of theset-delayed cement compositions may be activated to set to form ahardened mass in a time period in the range of from about 2 hours toabout 12 hours. For example, embodiments of the set-delayed cementcompositions may set to form a hardened mass in a time period rangingbetween any of and/or including any of about 2 days, about 4 days, about6 days, about 8 days, about 10 days, or about 12 days. After activation,the set-delayed cement composition may develop a 24-hour compressivestrength in the range of from about 50 psi to about 5000 psi,alternatively, from about 100 psi to about 4500 psi, or alternativelyfrom about 500 psi to about 4000 psi. In some embodiments, theset-delayed cement composition may develop a compressive strength in 24hours of at least about 50 psi, at least about 100 psi, at least about500 psi, or more. The compressive strengths may determined in accordancewith API RP 10B-2, Recommended Practice for Testing Well Cements, FirstEdition, July 2005, using an UCA at 140° F. while maintained at 3000psi.

Embodiments of the present invention may include addition of a cementset accelerator to the set-delayed cement compositions. Examples ofsuitable cement set accelerators include, but are not limited to,calcium chloride, triethanolamine, sodium silicate, zinc formate,calcium acetate, sodium hydroxide, sodium sulfate, and combinationsthereof The cement set accelerator should be added to embodiments of theset-delayed cement composition in an amount sufficient to activate theextended settable composition to set into a hardened mass. In certainembodiments, the cement set accelerator may be added to the set-delayedcement composition in an amount in the range of about 1% to about 20% byweight of the pumice. In specific embodiments, the cement setaccelerator may be present in an amount ranging between any of and/orincluding any of about 1%, about 5%, about 10%, about 15%, or about 20%by weight of the pumice. One of ordinary skill in the art, with thebenefit of this disclosure, will recognize the appropriate amount of thecement set accelerator to include for a chosen application.

As will be appreciated by those of ordinary skill in the art,embodiments of the set-delayed cement compositions of the presentinvention may be used in a variety of subterranean operations, includingprimary and remedial cementing. In some embodiments, a set-delayedcement composition may be provided that comprises water, pumice,hydrated lime, a set retarder, and optionally a dispersant. Theset-delayed cement composition may be introduced into a subterraneanformation and allowed to set therein. As used herein, introducing theset-delayed cement composition into a subterranean formation includesintroduction into any portion of the subterranean formation, including,without limitation, into a well bore drilled into the subterraneanformation, into a near well bore region surrounding the well bore, orinto both. Embodiments of the present invention may further includeactivation of the set-delayed cement composition. The activation of theset-delayed cement composition may comprise, for example, addition of acement set accelerator to the set-delayed cement composition.

In some embodiments, a set-delayed cement composition may be providedthat comprises water, pumice, hydrated lime, a set retarder, andoptionally a dispersant. The set-delayed cement composition may bestored, for example, in a vessel or other suitable container. Theset-delayed cement composition may be permitted to remain in storage fora desired time period. For example, the set-delayed cement compositionmay remain in storage for a time period of about 1 day or longer. Forexample, the set-delayed cement composition may remain in storage for atime period of about 1 day, about 2 days, about 5 days, about 7 days,about 10 days, about 20 days, about 30 days, about 40 days, about 50days, about 60 clays, or longer. In some embodiments, the set-delayedcement composition may remain in storage for a time period in a range offrom about 1 day to about 7 days or longer. Thereafter, the set-delayedcement composition may be activated, for example, by addition of acement set accelerator, introduced into a subterranean formation, andallowed to set therein.

In primary cementing embodiments, for example, embodiments of theset-delayed cement composition may be introduced into a space between awall of a well bore and a conduit (e.g., pipe strings, liners) locatedin the well bore, the well bore penetrating the subterranean formation.The set-delayed cement composition may be allowed to set to form anannular sheath of hardened cement in the space between the well borewall and the conduit. Among other things, the set cement composition mayform a barrier, preventing the migration of fluids in the well bore. Theset cement composition also may, for example, support the conduit in thewell bore.

In remedial cementing embodiments, a set-delayed cement composition maybe used, for example, in squeeze-cementing operations or in theplacement of cement plugs. By way of example, the set-delayedcomposition may be placed in a well bore to plug an opening, such as avoid or crack, in the formation, in a gravel pack, in the conduit, inthe cement sheath, and/or a microannulus between the cement sheath andthe conduit.

To facilitate a better understanding of the present invention, thefollowing examples of certain aspects of some embodiments are given. Inno way should the following examples be read to limit, or define, theentire scope of the invention.

EXAMPLE 1

The following series of tests was performed to evaluate the forceresistance properties of comparative cement compositions comprisingpumice and hydrated lime. Three different comparative sample settablecompositions, designated Samples 1-3, were prepared using pumice (DS-325lightweight aggregate), hydrated lime, Liquiment® 514L dispersant, andwater, as indicated in the table below. After preparation, the sampleswere placed in an UCA and cured at 140° F. and 3,000 psi for 24 hours.The cured cement was then removed from the UCA and crushed to yield thecompressive strength values provided in Table 1 below.

TABLE 1 Compressive Strength Tests Sample 1 2 3 Density lb/gal 14.3 14.314.3 Pumice:Lime Wt Ratio 3:1 4:1 5:1 Pumice g 400 400 400 Lime g 134103 100 Dispersant g 12 4 13 Water g 196 187 220 24-Hr Crush Strengthpsi 2,240 1,960 2,130

Example 1 thus indicates that cement compositions that comprise pumiceand lime in a weight ratio ranging from 3:1 to 5:1 may developcompressive strengths suitable for particular applications.

EXAMPLE 2

A sample set-delayed cement composition, designated Sample 4, having adensity of 13.3 lb/gal was prepared that comprised 500 grams of pumice(DS-325 lightweight aggregate), 100 grams of hydrated lime, 13 grams ofLiquiment® 514L dispersant, 24 grams of Micro Matrix® cement retarder,and 300 grams of water. The rheological properties of the sample weremeasured after storing at room temperature and pressure for periods of 1day and 6 days. After preparation, the rheological properties of thesample were determined at room temperature (e.g., about 80° F.) using aModel 35A Fann Viscometer and a No. 2 spring, in accordance with theprocedure set forth in API RP Practice 10B-2, Recommended Practice forTesting Well Cements. The results of this test are set forth in thetable below.

TABLE 2 Viscosity Tests Age of Yield Plastic Sample Fann Readings PointViscosity (days) 600 300 200 100 6 3 (lb/100 ft²⁾ (centipoise) 1 560 322244 170 46 38 84 238 6 498 310 228 136 24 20 122 188

Example 2 thus indicates that set-delayed cement compositions thatcomprise pumice, hydrated lime, a dispersant, a set retarder, and watercan remain fluid after 6 days.

EXAMPLE 3

A sample set-delayed cement composition, designated Sample 5, having adensity of 13.4 lb/gal was prepared that comprised 500 grams of pumice(DS-325 lightweight aggregate), 100 grams of hydrated lime, 7 grams ofLiquimene 514L dispersant, 6.3 grams of Micro Matrix® cement retarder,and 304 grams of water. The rheological properties of the sample weremeasured after storing at room temperature and pressure for periods offrom 1 day to 19 days. The rheological properties were measured at roomtemperature (e.g., about 80° F.) using a Model 35A Fann Viscometer and aNo. 2 spring, in accordance with the procedure set forth in API RPPractice 10B-2, Recommended Practice for Testing Well Cements. Theresults of this test are set forth in the table below.

TABLE 3 Viscosity Tests Age of Sample Fann Readings (Days) 300 200 100 63 1 462 300 130 12 8 2 458 282 122 6 4 5 420 260 106 3 2 8 446 270 110 41 12 420 252 100 3 2 19 426 248 94 2 1

After 7 days, calcium chloride in the amount indicated in Table 4 belowwas added to a separately prepared sample of the same formulation asabove. The sample was then placed in an UCA and the initial settingtime, which is the time for the composition to reach a compressivestrength of 50 psi while maintained at 3,000 psi was determined inaccordance with API RP Practice 10B-2, Recommended Practice for TestingWell Cements. The initial setting time of the sample was also determinedwithout addition of the calcium chloride. The samples with and withoutthe calcium chloride were heated to a temperature of 140° F. in 30minutes and then maintained at that temperature throughout the test.

TABLE 4 Compressive Strength Tests Age of Test CaCl₂ Initial SampleTemperature (% by wt of Setting Time (Days) (° F.) Pumice & Lime)(hr:min) 7 140 0 no set after 4 days 7 140 10 5:11

Example 3 thus indicates that the set-delayed cement compositions thatcomprise pumice, hydrated lime, a dispersant, a set retarder, and waterwill not set for a period of at least 19 days at ambient temperature andover 4 days at 140° F. Example 3 further indicates that sampleset-delayed cement compositions may be activated at a desired time byaddition of a suitable activator.

EXAMPLE 4

A sample set-delayed cement composition, designated Sample 6, having adensity of 13.4 lb/gal was prepared that comprised pumice (DS-325lightweight aggregate), 20% hydrated lime, 1.4% Liquiment® 514Ldispersant, 1.26% Micro Matrix® cement retarder, and 62% of water (allby weight of pumice, referred to in the table below as “% bwop”). After45 days in storage at ambient conditions, the sample was mixed with 6%calcium chloride. At 140° F., the sample had a thickening time (time to70 BC) of 2 hours and 36 minutes and an initial setting time (time to 50psi) of 9 hours and 6 minutes as measured using an UCA while maintainedat 3000 psi. After 48 hours, the sample was crushed with a mechanicalpress which gave a compressive strength of 2,240 psi. The thickeningtime and initial setting time were both determined in accordance withAPI RP Practice 10B-2, Recommended Practice for Testing Well Cements.The results of this test are set forth in the table below.

TABLE 5 Initial 48 Hr Age of Test Calcium Thickening Setting CrushSample Temperature Chloride Time Time Strength (Days) (° F.) (% bwop)(hr:min) (hr:min) (psi) 45 140 6 2:36 9:36 2,240

Example 4 thus indicates that the set-delayed cement compositions thatcomprise pumice, hydrated lime, a dispersant, a set retarder, and waterwill not set for a period of at least 45 days at ambient temperature.Example 4 further indicates that sample set-delayed cement compositionsmay be activated at a desired time by addition of a suitable activator.

EXAMPLE 5

This example was performed to evaluate the ability of sodium hydroxideand sodium sulfate to activate a set-delayed cement composition thatcomprised pumice (DS-325 lightweight aggregate), hydrated lime,Liquiment® 514L dispersant, Micro Matrix® cement retarder, and water.Four sample set-delayed cement compositions, designated Samples 7-10,were prepared having concentrations of components as indicated in thetable below. The samples were monitored via an UCA. After the sampleswere placed in the UCA, the pressure was increased to 3,000 psi, and thetemperature was increased to 100° F. over a 15-minute time period andheld for the duration of the test. A portion of the slurry was retainedand poured into a plastic cylinder to monitor the slurry behavior atroom temperature and pressure. These procedures were repeated for allsamples.

Sample 7 was monitored for 72 hours over which time no strength wasdeveloped and the slurry was still pourable when removed from the UCA.The portion kept at room temperature and pressure was likewise stillpourable after 72 hours.

Sample 8 was prepared using the same slurry design as Sample 7 exceptthat sodium hydroxide was added as an activator. The sodium hydroxidewas added in solid form directly to the mixing jar that contained theprepared sample. As can be seen from Table 6, Sample 8, reached 50 psiof compressive strength at 16 hours and 36 minutes. The strengthcontinued to build, reaching a maximum of 1,300 psi, when the test wasstopped at 72 hours. The cured cement was removed from the UCA andcrushed with a mechanical press which gave a compressive strength of 969psi. The portion kept at room temperature and pressure was crushed after7 days resulting in a compressive strength of 143 psi.

Sample 9 was prepared using the same slurry design as Sample 8 exceptthat sodium sulfate was added as an activator. The sodium sulfate wasadded in solid form directly to the mixing jar that contained theprepared slurry. Sample 9 reached 50 psi of compressive strength at 67hours and 29 minutes. The strength continued to build, slowly, reachinga maximum of 78 psi, when the test was stopped at 72 hours. The curedcement was removed from the UCA and crushed with a mechanical presswhich gave a compressive strength of 68.9 psi. The portion kept at roomtemperature and pressure was still too soft to be crushed after 7 days.

Sample 10 was prepared using the same slurry design as Sample 8 exceptthat equal amounts of sodium hydroxide and sodium sulfate were added asan activator. The sodium hydroxide and sodium sulfate were added insolid form directly to the mixing jar that contained the preparedslurry. Sample 10 reached 50 psi of compressive strength at 22 hours and40 minutes. The strength continued to build, reaching a maximum of 900psi, when the test was stopped at 72 hours. The cured cement was removedfrom the UCA and crushed with a mechanical press which gave acompressive strength of 786 psi. The portion kept at room temperatureand pressure was crushed after 7 days resulting in a compressivestrength of 47.9 psi.

The results of these tests are set forth in the table below. Theabbreviation “% bwop” refers to the percent of the component by weightof the pumice. The abbreviation “gal/sk” refers to gallons of thecomponent per 46-pound sack of the pumice. The abbreviation “RTP” refersto room temperature and pressure.

TABLE 6 Sample 7 8 9 10 Density lb/gal 13.38 13.38 13.38 13.38 Water %bwop 61.97 63.60 64.62 64.11 Pumice % bwop 100 100 100 100 Hydrated Lime% bwop 20 20 20 20 Dispersant gal/sk 0.07 0.07 0.07 0.07 Set Retarder %bwop 0.06 0.06 0.06 0.06 Sodium Hydroxide % bwop — 4 — 2 Sodium Sulfate% bwop — — 4 2 UCA Temp/Press F./Psi 100/ 100/ 100/ 100/ 3000 3000 30003000 Initial Set (50 psi) hr:min >78 16:36 67:29 22:40 Final Set (100psi) hr:min — 21:08 — 32:44 24 Hr Comp. Strength psi — 138.74 — 59.60 48Hr Comp. Strength psi — 711.35 — 331.48 72 Hr Comp. Strength psi — 130078 900 72 Hr Crush Strength psi — 969 68.90 786 (UCA) 7-Day CrushStrength psi — 143.20 0.00 47.90 (RTP)

Example 5 thus indicates that sodium hydroxide, sodium sulfate, andcombinations of the two can activate the set-delayed cementcompositions, but to varying degrees. The testing showed that bothsodium hydroxide and combinations of sodium hydroxide with sodiumsulfate activated the cement compositions to an acceptable level. Whencompared to the non-activated composition, sodium sulfate activated thecement compositions, but much less so than the sodium hydroxide orcombination of sodium hydroxide and sodium sulfate.

It should be understood that the compositions and methods are describedin terms of “comprising,” “containing,” or “including” variouscomponents or steps, the compositions and methods can also “consistessentially of” or “consist of” the various components and steps.Moreover, the indefinite articles “a” or “an,” as used in the claims,are defined herein to mean one or more than one of the element that itintroduces.

For the sake of brevity, only certain ranges are explicitly disclosedherein. However, ranges from any lower limit may be combined with anyupper limit to recite a range not explicitly recited, as well as, rangesfrom any lower limit may b,e combined with any other lower limit torecite a range not explicitly recited, in the same way, ranges from anyupper limit may be combined with any other upper limit to recite a rangenot explicitly recited. Additionally, whenever a numerical range with alower limit and an upper limit is disclosed, any number and any includedrange falling within the range are specifically disclosed. Inparticular, every range of values (of the form, “from about a to aboutb,” or, equivalently, “from approximately a to b,” or, equivalently,“from approximately a-b”) disclosed herein is to be Understood to setforth every number and range encompassed within the broader range ofvalues even if not explicitly recited. Thus, every point or individualvalue may serve as its own lower or upper limit combined with any otherpoint or individual value or any other lower or upper limit, to recite arange not explicitly recited.

Therefore, the present invention is well adapted to attain the ends andadvantages mentioned as well as those that are inherent therein. Theparticular embodiments disclosed above are illustrative only, as thepresent invention may be modified and practiced in different butequivalent manners apparent to those skilled in the art having thebenefit of the teachings herein. Although individual embodiments arediscussed, the invention covers all combinations of all thoseembodiments. Furthermore, no limitations are intended to the details ofconstruction or design herein shown, other than as described in theclaims below. Also, the terms in the claims have their plain, ordinarymeaning unless otherwise explicitly and clearly defined by the patentee.It is therefore evident that the particular illustrative embodimentsdisclosed above may be altered or modified and all such variations areconsidered within the scope and spirit of the present invention. Ifthere is any conflict in the usages of a word or term in thisspecification and one or more patent(s) or other documents that may beincorporated herein by reference, the definitions that are consistentwith this specification should be adopted.

What is claimed is:
 1. A method of cementing in a subterraneanformation, comprising: providing a set-delayed cement compositioncomprising water, pumice, hydrated lime, and a set retarder; activatingthe set-delayed cement composition; introducing the set-delayed cementcomposition into a subterranean formation; and allowing the set-delayedcement composition to set in the subterranean formation.
 2. The methodof claim 1 wherein the pumice has a mean particle size in a range ofabout 1 micron to about 200 microns.
 3. The method of claim 1 whereinthe pumice and the hydrated lime are present in a weight ratio of pumiceto hydrated lime of about 10:1 to about 1:1.
 4. The method of claim 1wherein the set retarder comprises at least one retarder selected fromthe group consisting of a phosphonic acid, a phosphonic acid derivative,a lignosulfonate, a salt, an organic acid, a carboxymethylatedhydroxyethylated cellulose, a synthetic co- or ter-polymer comprisingsulfonate and carboxylic acid groups, a borate compound, and any mixturethereof.
 5. The method of claim 1 wherein the set-delayed cementcomposition further comprises a dispersant.
 6. The method of claim 5wherein the dispersant comprises at least one dispersant selected fromthe group consisting of a sulfonated-formaldehyde-based dispersant, apolycarboxylated ether dispersant, and any combination thereof.
 7. Themethod of claim 1 wherein the set retarder comprises a phosphonic acidderivative, and wherein the set-delayed cement composition furthercomprises a polycarboxylated ether dispersant.
 8. The method of claim 7wherein the set-delayed cement comprise has a pumice-to-hydrated-limeweight ratio of about 3:1 to about 5:1, wherein set retarder is presentin an amount of about 0.01% to about 2% by weight of the pumice, andwherein the polycarhoxylated ether dispersant is present in an amount ofabout 0.01% to about 2% by weight of the pumice.
 9. The method of claim1 wherein the set-delayed cement composition further comprises at leastone additive selected from the group consisting of a weighting agent, alightweight additive, a gas-generating additive, amechanical-property-enhancing additive, a lost-circulation material, afiltration-control additive, a fluid-loss-control additive, a defoamingagent, a foaming agent, a thixotropic additive, and any combinationthereof.
 10. The method of claim 1 wherein the set-delayed cementcomposition remains in a pumpable fluid state for a time period of atleast about 7 days prior to the activating.
 11. The method of claim 1wherein the set-delayed cement composition remains in a pumpable fluidstate for a time period of at least about 30 days prior to theactivating.
 12. The method of claim 1 wherein the activating comprisesadding a cement set accelerator to the set-delayed cement composition.13. The method of claim 1 wherein the set-delayed cement compositionsets to develop a 24-hour compressive strength of at least about 50 psias measured using an Ultrasonic Cement Analyzer at 140° F. whilemaintained at 3,000 psi.
 14. The method of claim 1 wherein theset-delayed cement composition is introduced into a well borepenetrating the subterranean formation, the well bore having abottom-hole static temperature of less than about 200° F.
 15. The methodof claim 1 wherein the set-delayed cement composition is introduced intoan annulus between a wall of a well bore and a conduit disposed in thewell bore.
 16. A method of cementing in a subterranean formation,comprising: providing a set-delayed cement composition comprising water,pumice, hydrated lime, and a set retarder; storing the set-delayedcement composition for a period of at least about 1 day; adding a cementset accelerator to the set-delayed cement composition; introducing theset-delayed cement composition into a subterranean formation; andallowing the set-delayed cement composition to set in the subterraneanformation.
 17. The method of claim 16 wherein the pumice and thehydrated lime are present in a weight ratio of pumice to hydrated limeof about 10:1 to about 1:1.
 18. The method of claim 16 wherein the setretarder comprises a phosphonic acid derivative, and wherein theset-delayed cement composition further comprises a polycarboxylatedether dispersant.
 19. The method of claim 16 wherein the set-delayedcement composition further comprises a dispersant.
 20. The method ofclaim 16 wherein the set-delayed cement composition is stored for a timeperiod of at least about 30 days.
 21. A set-delayed cement compositioncomprising water; pumice; hydrated lime; and a set retarder, wherein theset-delayed cement composition will remain in a pumbable fluid state fora time period of at least about 1 day.
 22. The method of claim 21 theset-delayed cement composition further comprises a dispersant.